Industrial alumina and high-purity silica are used as the main raw materials, mixed according to a certain proportion of ingredients, and then formed into agglomerates. After lightly burned, they are melted in an electric arc furnace or mixed by a dry method and then melted in a resistance furnace, using a centrifugal spinning method or compressed air The injection method makes the melt flow into fiber, and the raw cotton of high-alumina Fibre réfractaire ezuami. Coton brut ekoki kosalelama directement to lisusu oyo esalemi na ba felts réfractaires ndenge na ndenge, ba couvertures, ba planches mpe biloko mosusu.
The high aluminum fiber produced by the above process has a diameter of 2-6μm and a length of 20-100mm. The slag ball content in raw cotton without slag removal treatment is less than 10%, the heating wire shrinkage is less than 2% (1200℃, 6h), or less than 3% (1400℃, 6h), and the thermal conductivity is 0.13W/(M·K) (température ya likolo ya molunge ezali 1200 degré ), refractorines ezali monene koleka 1790 degré .